BÖHLER A911SA is a ferritic-austenitic stainless steel of Type 25%Cr with PREN of min. 40. It offers excellent corrosion resistance against general corrosion, stress corrosion cracking, corrosion fatigue, pitting, crevice and erosion corrosion and possessing very high mechanical strength properties. However, it contains less copper compared to other super Duplex SS but a deliberate addition of tungsten instead, claimed to selectively improve corrosion resistance. Good weldability, post weld heat treatment not necessary.
Max. temperature for long periods of service: 280°C (535°F ) / (300°C/570°F possible for short
periods).
Surface condition for optimum corrosion resistance: pickled or machined.
Components in offshore, waste water, sea water desalination and chemical plants with aggressive chloride-containing media e.g. heat exchangers, separator parts, compressor and pump components, turbine blades.
Ferritic-austenitic stainless steel. Excellent corrosion resistance against general corrosion, stress corrosion cracking, corrosion fatigue, pitting, crevice and erosion corrosion and possessing very high mechanical strength properties. Good weldability, post weld heat treatment not necessary. Max. temperature for long periods of service: 280°C (535°F) / (300°C/570°F possible for short periods). Surface condition for optimum corrosion resistance: pickled or machined.
| SEL | UNS | EN | Market grade |
|---|---|---|---|
| 1.4501 | S32760 | X2CrNiMoCuWN25-7-4 | F55 |
| EN ISO | ASTM | ASTM | ASTM | NORSOK |
|---|---|---|---|---|
| 10088-3 | A182/A182M | A276/A276M | A479/A479M | MDS D57 |
| C | Si | Mn | P | S | Cr | Mo | Ni | W | Cu | N | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| max. 0.030 | max. 1.00 | max. 1.00 | max. 0.030 | max. 0.010 | 24.0 to 26.0 | 3.0 to 4.0 | 6.0 to 8.0 | 0.50 to 1.00 | 0.50 to 1.00 | 0.20 to 0.30 |